EN 10326:2004

Continuously hot-dip coated strip and sheet of structural steels - Technical delivery conditions

Publication date:   Sep 30, 2005

General information

99.60 Withdrawal effective   Mar 11, 2009

CEN

CEN/TC 459/SC 9 Coated and uncoated flat products to be used for cold forming

European Norm

77.140.10   Heat-treatable steels | 77.140.50   Flat steel products and semi-products

Buying

  Withdrawn

PDF - €31.61

  English  



Buy

Scope

1.1 This European Standard specifies requirements for continuously hot-dip coated products made of structural steels coated with zinc (Z), zinc-iron alloy (ZF), zinc-aluminium alloy (ZA), aluminium-zinc alloy (AZ) and aluminium-silicon alloy (AS) (see Table 1) with thicknesses from 0,35 mm up to 3,0 mm unless otherwise agreed (see 1.2). The thickness is the final thickness of the delivered product after coating.
This European Standard applies to strip of all widths and to sheets cut from it (= 600 mm width) and cut lengths
(< 600 mm width).
1.2 If agreed at the time of enquiry and order, this European Standard may also be applied to continuously hot-dip coated flat products in thicknesses > 3,0 mm. In this case the mechanical property, adhesion of coating and surface condition requirements shall also be agreed at the time of enquiry and order.
1.3 The products covered by this European Standard are mainly used where minimum yield strength and corrosion resistance are the most important factors. Corrosion resistance of the alloy is proportional to the coating thickness, hence to its mass (see also 7.3.2).
NOTE +ZF coated products should not be used without additional organic coating.
1.4 This European Standard is not applicable to:
· continuously hot-dip coated flat products of low-carbon steel strip and sheet for cold forming (see prEN 10327);
· electrolytic galvanized cold rolled steel flat products (see EN 10152);
· continuously organic coated (coil coated) flat steel products (see EN 10169-1, ENV 10169-2 and
EN 10169-3);
· continuously hot-dip coated strip and sheet of steels with higher yield strength for cold forming (see EN 10292).

Life cycle

PREVIOUSLY

WITHDRAWN
EN 10214:1995

WITHDRAWN
EN 10215:1995

WITHDRAWN
EN 10147:2000

WITHDRAWN
EN 10154:2002

NOW

WITHDRAWN
EN 10326:2004
99.60 Withdrawal effective
Mar 11, 2009

REVISED BY

WITHDRAWN
EN 10346:2009